| PA66 408L 美国杜邦公司 物性数据 |
| 规格级别： | 特殊级 | 外观颜色： | --- |
| 用途概述： | 适合超高抗冲击性的工程制品 | ||
| 备注说明： | --- |
| 性能项目 | 试验条件[状态] | 测试方法 |
| 数据单位 | |||
| 基本性能 | 吸水率 | 24hr | ASTM D-570 | 1.2 | % | ||
| 物理性能 | 模具收缩率 | 3.2mm | --- |
| % | ||
| 阻燃性 | --- | UL 94 |
| mm | |||
| 比重 | --- | ASTM D-792 |
| --- | |||
| 阻燃性 | --- | UL 94 | HB | --- | |||
| 机械性能 | 拉伸强度 | 23℃ | ASTM D-638 |
| MPa | ||
| 拉伸屈服强度 | --- | ASTM D-638 |
| MPa | |||
| 断裂伸长率 | --- | ASTM D-638 |
| % | |||
| 屈服伸长率 | --- | ASTM D-638 |
| % | |||
| 弯曲模量 | --- | ASTM D-790 |
| MPa | |||
| IZOD冲击强度 | --- | ASTM D-256 |
| J/m | |||
| 电气性能 | 体积电阻率 | --- | ASTM D-257 |
| Ω.cm | ||
| 热 性 能 | 熔点 | --- | ASTM D-3418 |
| ℃ | ||
| 热变形温度 | 0.45MPa | ASTM D-648 |
| ℃ | |||
| 热变形温度 | 1.80MPa | ASTM D-648 |
| ℃ | |||
| 其它性能 | CLTE | --- | ASTM D-696 |
| 10-4/K |